Al 99.98% Ø6x13mm 1kg - 0481946

Al 99.98% Ø6x13mm 1kg - 0481946

Specifications

Coating material

Aluminium

Purity

99.98%

Form

Rod

Dimensions

Ø 6 x 13 mm

Quantity

1 kg

Theoretical density at 20°C in g/cm³

2.7

Melting point in °C

660

Temperature at vapor pressure

10⁻² mbar in °C

1210

10⁻¹ mbar in °C

1360

Boiling point in °C

2467

Type of evaporation

Melting

Good

Evaporation source (typically)

E-gun

Directly from Cu crucible

Good

Liner material

C

Good

BN

Good

Boat

Boat material

W

Possible

Specific evaporation conditions

Preparation of base melt (premelt)

Good

Low residual pressure

Good

Film refractive index n / extinction coefficient k

at 550 nm: n

0.76-0.95

at 550 nm: k

5.50-6.99

at 10 µm: n

25.3

at 10 µm: k

89.8